[Nature Communications] 我室董全峰教授和毛秉伟教授发表论文:Designable ultra-smooth ultra-thin solid-electrolyte interphases of three alkali metal anodes

2018年04月10日

我室董全峰教授和毛秉伟教授在 Nature Communications 上发表论文:Designable ultra-smooth ultra-thin solid-electrolyte interphases of three alkali metal anodes

文章链接:https://www.nature.com/articles/s41467-018-03466-8

摘要:

Dendrite growth of alkali metal anodes limited their lifetime for charge/discharge cycling. Here, we report near-perfect anodes of lithium, sodium, and potassium metals achieved by electrochemical polishing, which removes microscopic defects and creates ultra-smooth ultra-thin solid-electrolyte interphase layers at metal surfaces for providing a homogeneous environment. Precise characterizations by AFM force probing with corroborative in-depth XPS profile analysis reveal that the ultra-smooth ultra-thin solid-electrolyte interphase can be designed to have alternating inorganic-rich and organic-rich/mixed multi-layered structure, which offers mechanical property of coupled rigidity and elasticity. The polished metal anodes exhibit significantly enhanced cycling stability, specifically the lithium anodes can cycle for over 200 times at a real current density of 2 mA cm–2 with 100% depth of discharge. Our work illustrates that an ultra-smooth ultra-thin solid-electrolyte interphase may be robust enough to suppress dendrite growth and thus serve as an initial layer for further improved protection of alkali metal anodes.